Chartwell 제품의 물성(Properties)

Generally 1.0 phr to 2.0 phr is recommended. The presence of high surface area pigment (.ie. carbon black, fine organics, fumed silica) requires the use of 1.0 - 2.0% based upon combined resin solids plus pigment weight to achieve comparable results.

​Chartwell 제품의 물성(Properties)

​

(ㄱ)  H,HR and Standard Grades의 일반적 물성
(ㄴ)  고함량 " 2H" & "H" 제품
(ㄷ)  Chartwell 사용량과 접착향상과의 관계(Use Levels)
(ㄹ)  Silane 경쟁제품 비교
(ㅁ)  사용순서
(ㅂ)  유기관능기(Organoreactive Groups)

​

           (ㄱ)  H,HR and Standard Grades의 일반적 물성



















































































































      1.     다른 금속의 수를 표시한다

        * Denotes tentative specifications
      ** pH1% Solution

    
          (ㄴ)고함량 " 2H" & "H" 제품     

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​

​





​

            1. 다른 금속의 수를 표시한다

              *  Denotes tentative specifications.
            **  Denotes pH1% Solution
                 모든 Chartsil 제품은 “H” 등급으로 이용가능하다.
                 Chartsil: 72% (+/- 2%)  Chartwell liquid, 28% silica
 

       (ㄷ)Chartwell 사용량과 접착향상과의 관계(Use Levels)

































































       (ㄹ)Silane 경쟁제품 비교



























































  

​                                                   * 차트웰 제품은 액상 및 고체(분말)형태의 제품을 모두 이용 가능하다.

​

  

      (ㅁ)사용순서 (Use Procedure)

Generally 1.0 phr to 2.0 phr is recommended. The presence of high surface area pigment (.ie. carbon black, fine organics, fumed silica) requires the use of 1.0 - 2.0% based upon combined resin solids plus pigment weight to achieve comparable results.

코팅(COATINGS0, 접착제(ADHESIVES), 잉크및도료(INKS)
용매제(SOLVENT BORNE): Addition to the grind stage with high shear mixing is strongly recommended.
수용제(WATER BORNE): Water-borne formulations will generally require 1.0-3.0 wt per cent based upon binder solids and organic pigment weight, anti-corrosive pigment weight, and carbon black. Post add or add to grind.

​

고무화합물(RUBBER COMPOUNDS), 분말코팅(POWDER COATINGS)
It is recommended that the Chartwell product be added directly upon the silica (or other mineral), and thereafter, the mix compounded in a Banbury/ Henschel as would be conventionally done.
Evaluation at 1.0, 2.0, and3.0 phr is recommended for Chartwell (liquid) products.Evaluation at 1.5 and 3.0 phr is recommended for Chartsil (solid) products. Torque and shear should be maximized.



열소성 수지, 무기물 표면 처리 및 다른 응용:
기술 지원을 위해 상담하십시오.(02-552-1420)​
 

     (ㅂ)유기관능기(Organoreactive Groups)